Density
|
Ash Cont.
|
Hardness
Shore
|
Yield stress
|
Elonga-
tion At Break
|
Flex.
Strength
|
Notched
Impact
Strength
|
Vicat
Softening Temp.
|
HDT
|
Melting Range
|
Flamma-
bility
|
|
Test Methods
|
ISO
1183
|
ISO 3451
|
ISO 868
|
ISO 527
|
ISO527
|
ISO178
|
ISO180/A
|
ISO 306
|
ISO75 A/B
|
|
UL 94
|
|
UNIT
|
g /cm³
|
%
|
D
|
MPa
|
%
|
MPa
|
Kj / m²
|
°C
|
°C
|
°C
|
|
|
UNR
|
PA 66 UNR
|
1. 14
|
|
83
|
84
|
10
|
120
|
4. 8
|
240
|
96/215
|
255– 260
|
V2
|
|
Glass
Fiber
Reinfor
|
PA 66 GFR 15
|
1. 23
|
15
|
84
|
130
|
3
|
190
|
6
|
245
|
250
|
255– 260
|
HB
|
|
PA 66 GFR 25
|
1. 30
|
25
|
84
|
150
|
3
|
235
|
8
|
250
|
250
|
255– 260
|
HB
|
|
PA 66 GFR 33
|
1. 37
|
33
|
85
|
165
|
3
|
275
|
10. 5
|
250
|
|
255 – 260
|
HB
|
|
Mine –ral
reinforcement
|
PA 66 MNF 20
|
1. 28
|
20
|
80
|
75
|
4
|
120
|
2. 5
|
235
|
|
255 – 260
|
HB
|
|
PA 66
MNF 30
|
1. 36
|
30
|
81
|
80
|
3
|
130
|
3
|
240
|
230
|
255– 260
|
HB
|
|
PA 66 MNF 40
|
1. 45
|
40
|
82
|
85
|
2. 5
|
145
|
4
|
250
|
|
255– 260
|
HB
|
|
Flame Retard.
|
PA 66 FR Vo
|
1. 51
|
20
|
82
|
85
|
3
|
|
6.5
|
|
|
255– 260
|
Vo
|
|
|
|